VALOX(沙伯基础)VX5022/PBT热塑性聚酯/物性表参数
沙伯基础创新塑料SABIC的VALOX VX5022 PBT是一种加20%玻璃纤维增强PBT+PC共混物，具有低翘曲性能,这个等级是5021，减少翘曲。
 |
沙伯基础创新塑料的VALOX VX5022 PBT物性表参数PDF文档下载 |
以下是VALOX(沙伯基础)VX5022/PBT热塑性聚酯/物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 125 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 125 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 7300 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 145 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5800 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 110 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 110 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 7100 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 6300 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 205 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 122 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 55 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 50 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 650 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 645 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 80 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 65 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 200 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 180 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 4.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 2.49E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.87E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.43E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.12E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 200 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 145 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 180 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.39 | - | ASTM D 792 | |
| Filler Content | 20 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.8 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.3-0.5 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-0.9 | % | SABIC method | |
| Melt Flow Rate, 250°C/2.16 kgf | 16 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 265°C/5.0 kgf | 50 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 266°C/5.0 kgf | 50 | g/10 min | ASTM D 1238 | |
| Density | 1.39 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.1 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 13 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 28 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 40 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 215 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 31 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.3 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.014 | - | ASTM D 150 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+16 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+16 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 31 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 100 Hz | 3.3 | - | IEC 60250 | |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 100 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 | |
| Comparative Tracking Index, M | 100 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Flammability Index 850°C, passes at | 2 | mm | IEC 60695-2-12 | |
| Oxygen Index (LOI) | 23 | % | ISO 4589 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：8191 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：7856 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：6675 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：6360 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：5846 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：5235 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：5019 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：4717 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：4662 -
COC(环烯烃共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一种烯烃聚合物(COP)具有优异的光学性能，可用于制造相机和激光打印机的光学部件，比重是1.01g/cm(ASTM D792)，熔流率（熔体流动速率）(280C/2.16 kg)是25g/10 min，ZEO
浏览量：4640 -
PC(聚碳酸酯)L-1250Y|嘉兴帝人|物性表参数嘉兴帝人Panlite PC L-1250Y 是一款熔融体积流量是8MVR，特性是 脱模性能良好, 中等粘性 ，通用级应用，在Japan实现工业化生产的聚碳酸酯树脂，长期以来，帝人一直致力于其性能的提高和
浏览量：4468 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：4452 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：4446 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：4389 -
PC(聚碳酸酯)PC-1100|乐天化学(LOTTE CHEMI···乐天化学的LOTTE Chemical HOPELEX PC PC-1100 是一种聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高强度、FDA/EU 食品容器认证，用于普通注塑产品。 以下是PC(聚碳酸酯)PC-1100/韩国乐天化学
浏览量：4271
推荐文章
-
PC(聚碳酸酯)2558/科思创(Makrolon)物性表参数
科思创(Covestro)模克隆(Makrolon) PC 2558 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 14cm cm /10 min，中粘度，用于121℃的ETO和蒸汽灭菌;符合多项ISO 10993-1测试要求的生物相容性，应用于医
-
PP(聚丙烯)BJ355/韩华道达尔/物性表参数
韩华道达尔嵌段 PP BJ355 是适用于注塑成型用途，恰当的橡胶设计使BJ355具有优异的刚性和冲击强度平衡性.其特点是：高刚性、高冲击强度、易脱模特定。 韩华道达尔PP BJ355物性表参数
-
POM(聚甲醛树脂)9054|旭化成(AsahiKASEI)物性表参数
旭化成(AsahiKASEI)TENAC(铁耐克)POM 9054是超高流量等级，具有高结晶率，抗静电性能，可提高生产效率的聚甲醛树脂，密度 1.42(g/cm³)，弯曲模量3300(MPa) ，简支梁缺口冲击强度4.0(kJ/m²) ，典型用途领域包括工程/工业配件、房屋和汽车行业。TENAC POM 9054 ISO参数PDF文档以下是POM(聚甲醛树脂)9054|旭化成(AsahiKASE
-
PC/ABS(PC+ABS合金)T-2830R|TEIJIN(帝人)物性表参数
TEIJIN(帝人)Multilon PC/ABS T-2830R 是一款流动性高,耐低温冲击,耐热性高 的 PC合金材料, 应用于 汽车内部零件,汽车外部零件,汽车仪表板 ， Multilon是帝人株式会社开发的PC/ABS系列的聚合物合金
-
PC(聚碳酸酯)FXD1414T/沙伯基础(SABIC)物性表参数
SABIC(沙伯基础创新塑料)LEXAN PC FXD1414T 是透明PC加硅氧烷共聚物，加工性能优异，具有特殊的光扩散颜色，低流动性。与相同颜色的标准PC相比，提高了韧性。 PC(聚碳酸酯)FXD1414T/沙伯基础
-
POM(聚甲醛共聚物)M450/塞拉尼斯(CELANESE)物性表参数
塞拉尼斯(CELANESE)Celcon POM M450是一种超高流动聚甲醛共聚物，密度是1.41g/cm³，溶化体积流率（MVR）(190°C/2.16 kg)是39.0cm³/10min，在非常薄壁或长，狭窄的注射成型流道中具有最佳的循环性能。以下是POM(聚甲醛共聚物)M450/塞拉尼斯(CELANESE)物性表参数基本信息黄卡编号E38860-239311E38860-101305515特性低粘
-
PPA(聚邻苯二甲酰胺)GV-2FWA|艾曼斯|物性表参数
艾曼斯Grivory PPA GV-2FWA材料是一种Polyamide 66 + PA 6I/X (Nylon 66+Nylon 6I/X)材料,含有的填充物为20% 玻璃纤维增强材料。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,加工
-
PC(聚碳酸酯)PC1003R|SABIC(沙伯基础)物性表参数
沙伯基础SABIC塑料 PC PC1003R 是 一种 中低流动（MFR = 10,300℃/ 1.2kg），耐热和紫外线稳定的聚碳酸酯产品，具有脱模剂，设计用于通用模塑市场。 沙伯基础SABIC塑料PC PC1003R物性表参数PDF文
-
PC(聚碳酸酯)N-9|三菱工程塑料|物性表参数
三菱工程塑料Iupilon/NOVAREX/XANTAR PC N-9是阻燃透明挤出品级; 体积熔融指数3.3厘米3/10分钟; 普通用途; 易脱模; 注塑成型,三菱工程研究开发成功的聚碳酸酯，在市场上已有好多年历史, 被广泛地用于各种工业生产，如运动器械、医疗器械、汽车部件、光学仪器、机械、办公自动化设备和电子设备，获得了客户的广泛信赖和支持,
-
COC(环烯烃共聚物)8007F-600|宝理塑料|物性表参数
宝理塑料TOPAS COC 8007F-600是一种新的坚固的薄膜挤出等级，设计用于与聚乙烯(PE)共混，它是一种提高透明度的非晶树脂，具有高硬度，防潮，耐化学反应，热成型性和纯度，适用于食品和一般用途，它用于铸造和吹制过程中的共混物，以及单层和多层产品，主要的薄膜应用包括扭转包装，成型网，保护性包装，收缩薄膜和标签，易撕