德国朗盛LANXESS Durethan PA6 BKV30H2.0LT是一种加入30%玻璃纤维，注塑，改善流动性，热老化稳定,透明着色(黑)尼龙6树脂，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
PA6 BKV30H2.0LT

以下是PA6(尼龙6)BKV30H2.0LT/德国朗盛/物性表参数

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 280 °C / MT 80 °C; 500 bar	%	acc. ISO 2577	0.18
	Molding shrinkage, transverse	150x105x3; 280 °C / MT 80 °C; 500 bar	%	acc. ISO 2577	0.85
	Post- shrinkage, parallel	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.04
	Post- shrinkage, transverse	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.11
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	9500	5900
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	170	100
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.0	6.0
	Tensile creep modulus	1 h	MPa	ISO 899-1		5100
	Tensile creep modulus	1000 h	MPa	ISO 899-1		4100
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	80	90
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	70	70
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	10	20
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10	<10
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	8300	5000
	Flexural strength	2 mm/min	MPa	ISO 178-A	270	160
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	4.0	6.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A		140
	Puncture energy	23 °C	J	ISO 6603-2	6	10
	Puncture energy	-30 °C	J	ISO 6603-2	4
	Ball indentation hardness		N/mm²	ISO 2039-1	210	100
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	~200
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	~215
	Temperature of deflection under load	8.00 MPa	°C	ISO 75-1,-2	~110
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	>200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.2
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.8
	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
	Burning behavior UL 94	3.2 mm	Class	UL 94	HB
	Oxygen index	Method A	%	ISO 4589-2	22
	Glow wire test (GWFI)		°C	IEC 60695-2-12	600
	Burning behavior US-FMVSS302			ISO 3795	passed
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	4.2	12
	Relative permittivity	1 MHz	-	IEC 60250	3.8	4.4
	Dissipation factor	100 Hz	10-4	IEC 60250	100	2550
	Dissipation factor	1 MHz	10-4	IEC 60250	170	780
	Volume resistivity		Ohm·m	IEC 60093	1E13	1E10
	Surface resistivity		Ohm	IEC 60093	1E14	1E13
	Electric strength	1 mm	kV/mm	IEC 60243-1	40	35
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	425
	Comparative tracking index CTI M	Solution B	Rating	IEC 60112	300 (200) M 1.4
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	~7.0
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	~2.1
	Density		kg/m³	ISO 1183	1360
	Bulk density		kg/m³	ISO 60	~700
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	270-290
	Mold temperature		°C	-	80-120

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.

上一页：PA6(尼龙6)BKV30H2.0EF/德国朗盛/物性表参数下一页：PA6(尼龙6)BKV30H2.0XF/德国朗盛/物性表参数

返回首页返回物性参数列表

PA6(尼龙6)BKV30H2.0LT/德国朗盛/物性表参数

热门文章

推荐文章