PA6(尼龙6)BM240H3.0/德国朗盛/物性表参数

日期：2020-04-14 10:11:03 编辑：科思德塑胶来源：科思德塑胶浏览：317

德国朗盛LANXESS Durethan PA6 BM240H3.0是一种加入40%矿物填充，注塑，不易变形，热老化稳定尼龙6树脂，尼龙从环境中吸收潮气的能力也不同,这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
PA6 BM240H3.0

以下是PA6(尼龙6)BM240H3.0/德国朗盛/物性表参数

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.85
	Molding shrinkage, transverse	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.85
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.25
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.25
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	5700	2200
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	85	55
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	5.5	40
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	150	N
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	130	80
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	< 10	12
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	< 10	< 10
	Charpy notched impact strength	-40 °C	kJ/m²	ISO 179-1eA	< 10	< 10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	130	N
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	100	85
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	< 10	< 10
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	< 10	< 10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	5500	2000
	Flexural strength	2 mm/min	MPa	ISO 178-A	140	65
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	5.5	8.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	130	60
	Puncture maximum force	23 °C	N	ISO 6603-2	3030
	Puncture maximum force	-30 °C	N	ISO 6603-2	728
	Puncture energy	23 °C	J	ISO 6603-2	20	65
	Puncture energy	-30 °C	J	ISO 6603-2	3
	Ball indentation hardness		N/mm²	ISO 2039-1	205	85
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	85
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	185
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	> 200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.6
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.7
	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
	Burning behavior UL 94	0.75 mm	Class	UL 94	HB
	Oxygen index	Method A	%	ISO 4589-2	27
	Glow wire test (GWFI)	2.0 mm	°C	IEC 60695-2-12	650
	Burning behavior US-FMVSS302			ISO 3795	passed
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	4.5
	Relative permittivity	1 MHz	-	IEC 60250	4.0
	Dissipation factor	100 Hz	10-4	IEC 60250	255
	Dissipation factor	1 MHz	10-4	IEC 60250	240
	Volume resistivity		Ohm·m	IEC 60093	4E13
	Surface resistivity		Ohm	IEC 60093	7E15
	Electric strength	1 mm	kV/mm	IEC 60243-1	36
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	550
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	6.0
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.9
	Density		kg/m³	ISO 1183	1440
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	290
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	280-300
	Mold temperature		°C	-	80-120