PA66(尼龙66)22G5/长春化工(漳州)/物性表参数
以下是PA66(尼龙66)22G5/长春化工(漳州)/物性表参数
| 密度 | 1.35 g/cc | 0.0488 lb/in³ | |
| 1.49 g/cc | 0.0538 lb/in³ | DAM; ISO 1183 | |
| 吸水率 |
3.4 %
@Thickness 2.00 mm
|
3.4 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 水分吸收 |
0.900 %
@Thickness 2.00 mm
|
0.900 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 粘度 |
85370 cP
@Shear Rate 5000 1/s, Temperature 280 °C
|
85370 cP
@Shear Rate 5000 1/s, Temperature 536 °F
|
ISO 11403-1 -2 |
|
138900 cP
@Shear Rate 5000 1/s, Temperature 270 °C
|
138900 cP
@Shear Rate 5000 1/s, Temperature 518 °F
|
ISO 11403-1 -2 | |
|
243400 cP
@Shear Rate 5000 1/s, Temperature 260 °C
|
243400 cP
@Shear Rate 5000 1/s, Temperature 500 °F
|
ISO 11403-1 -2 | |
|
270750 cP
@Shear Rate 500 1/s, Temperature 280 °C
|
270750 cP
@Shear Rate 500 1/s, Temperature 536 °F
|
ISO 11403-1 -2 | |
|
441600 cP
@Shear Rate 500 1/s, Temperature 270 °C
|
441600 cP
@Shear Rate 500 1/s, Temperature 518 °F
|
ISO 11403-1 -2 | |
|
774800 cP
@Shear Rate 500 1/s, Temperature 260 °C
|
774800 cP
@Shear Rate 500 1/s, Temperature 500 °F
|
ISO 11403-1 -2 | |
| 粘度测试 | 140 cm³/g | 140 cm³/g | DAM; ISO 307 1157 1628 |
| 线性成型收缩率,Flow | 0.0020 cm/cm | 0.0020 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.010 cm/cm | 0.010 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 110 MPa | 16000 psi | 50%RH; ISO 527-1/-2 |
| 125 MPa | 18100 psi | DAM; ISO 527-1/-2 | |
| 抗张强度 |
8.79 MPa
@Strain 0.230 %, Temperature 150 °C
|
1270 psi
@Strain 0.230 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 |
|
12.0 MPa
@Strain 0.240 %, Temperature 90.0 °C
|
1740 psi
@Strain 0.240 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
|
15.95 MPa
@Strain 0.470 %, Temperature 150 °C
|
2313 psi
@Strain 0.470 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
22.76 MPa
@Strain 0.480 %, Temperature 90.0 °C
|
3301 psi
@Strain 0.480 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
|
24.06 MPa
@Strain 0.700 %, Temperature 150 °C
|
3490 psi
@Strain 0.700 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
|
25.92 MPa
@Strain 0.400 %, Temperature 40.0 °C
|
3759 psi
@Strain 0.400 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
|
31.12 MPa
@Strain 1.10 %, Temperature 150 °C
|
4514 psi
@Strain 1.10 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
34.25 MPa
@Strain 0.790 %, Temperature 90.0 °C
|
4968 psi
@Strain 0.790 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
|
37.13 MPa
@Strain 0.540 %, Temperature 40.0 °C
|
5385 psi
@Strain 0.540 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
|
41.37 MPa
@Strain 0.570 %, Temperature 23.0 °C
|
6000 psi
@Strain 0.570 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
|
41.5 MPa
@Strain 0.470 %, Temperature 23.0 °C
|
6020 psi
@Strain 0.470 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
|
42.25 MPa
@Strain 1.55 %, Temperature 150 °C
|
6128 psi
@Strain 1.55 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
|
44.11 MPa
@Strain 2.01 %, Temperature 150 °C
|
6398 psi
@Strain 2.01 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
44.88 MPa
@Strain 1.15 %, Temperature 90.0 °C
|
6509 psi
@Strain 1.15 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
|
52.61 MPa
@Strain 3.26 %, Temperature 150 °C
|
7630 psi
@Strain 3.26 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
54.28 MPa
@Strain 0.980 %, Temperature 40.0 °C
|
7873 psi
@Strain 0.980 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
|
55.02 MPa
@Strain 2.75 %, Temperature 150 °C
|
7980 psi
@Strain 2.75 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
|
57.51 MPa
@Strain 1.63 %, Temperature 90.0 °C
|
8341 psi
@Strain 1.63 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
|
63.12 MPa
@Strain 2.08 %, Temperature 90.0 °C
|
9155 psi
@Strain 2.08 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
|
63.72 MPa
@Strain 0.650 %, Temperature -20.0 °C
|
9242 psi
@Strain 0.650 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
|
67.98 MPa
@Strain 0.820 %, Temperature 0.000 °C
|
9860 psi
@Strain 0.820 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
|
71.93 MPa
@Strain 3.50 %, Temperature 90.0 °C
|
10430 psi
@Strain 3.50 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
|
72.3 MPa
@Strain 0.770 %, Temperature 0.000 °C
|
10500 psi
@Strain 0.770 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
|
73.4 MPa
@Strain 1.26 %, Temperature 40.0 °C
|
10600 psi
@Strain 1.26 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
|
73.91 MPa
@Strain 1.18 %, Temperature 23.0 °C
|
10720 psi
@Strain 1.18 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
|
74.49 MPa
@Strain 2.80 %, Temperature 90.0 °C
|
10800 psi
@Strain 2.80 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
|
78.89 MPa
@Strain 0.830 %, Temperature -20.0 °C
|
11440 psi
@Strain 0.830 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
|
79.11 MPa
@Strain 1.75 %, Temperature 40.0 °C
|
11470 psi
@Strain 1.75 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
|
84.04 MPa
@Strain 1.04 %, Temperature 23.0 °C
|
12190 psi
@Strain 1.04 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
|
94.42 MPa
@Strain 2.82 %, Temperature 40.0 °C
|
13690 psi
@Strain 2.82 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
|
100.33 MPa
@Strain 1.96 %, Temperature 23.0 °C
|
14552 psi
@Strain 1.96 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
|
100.68 MPa
@Strain 1.34 %, Temperature 0.000 °C
|
14602 psi
@Strain 1.34 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
|
100.92 MPa
@Strain 2.18 %, Temperature 40.0 °C
|
14637 psi
@Strain 2.18 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
|
101.62 MPa
@Strain 1.11 %, Temperature -20.0 °C
|
14739 psi
@Strain 1.11 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
|
118.66 MPa
@Strain 1.78 %, Temperature 23.0 °C
|
17210 psi
@Strain 1.78 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
|
120.54 MPa
@Strain 1.46 %, Temperature 0.000 °C
|
17483 psi
@Strain 1.46 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
|
127.28 MPa
@Strain 1.98 %, Temperature 0.000 °C
|
18460 psi
@Strain 1.98 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
|
134.63 MPa
@Strain 1.66 %, Temperature -20.0 °C
|
19526 psi
@Strain 1.66 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
|
142.85 MPa
@Strain 1.74 %, Temperature -20.0 °C
|
20719 psi
@Strain 1.74 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
|
157.09 MPa
@Strain 2.33 %, Temperature 0.000 °C
|
22784 psi
@Strain 2.33 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 伸长率 (断裂) | 2.0 % | 2.0 % | DAM; ISO 527-1/-2 |
| 2.6 % | 2.6 % | 50%RH; ISO 527-1/-2 | |
| 拉伸模量 | 7.50 GPa | 1090 ksi | 50%RH; ISO 527-1/-2 |
| 9.00 GPa | 1310 ksi | DAM; ISO 527-1/-2 | |
|
3.213 GPa
@Temperature 150 °C
|
466.0 ksi
@Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
3.595 GPa
@Temperature 150 °C
|
521.4 ksi
@Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
|
5.515 GPa
@Temperature 60.0 °C
|
799.9 ksi
@Temperature 140 °F
|
50%RH; ISO 11403-1 -2 | |
|
5.62 GPa
@Temperature 60.0 °C
|
815 ksi
@Temperature 140 °F
|
DAM; ISO 11403-1 -2 | |
|
10.386 GPa
@Temperature -20.0 °C
|
1506.4 ksi
@Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
|
10.498 GPa
@Temperature -20.0 °C
|
1522.6 ksi
@Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 割线模量 |
4.16 GPa
@Strain 2.06 %, Temperature 40.0 °C
|
603 ksi
@Strain 2.06 %, Temperature 104 °F
|
 |
PA66(尼龙66)22G5/长春化工(漳州)/物性表参数 |
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：10606 -
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：9690 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：9196 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：7821 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：7225 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：6879 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：6552 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：6042 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：5937 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：5663 -
PA12(尼龙12)TR90|瑞士EMS化学|物性表参数科思德塑胶网站提供瑞士EMS化学PA12 TR90的物性表参数下载，并且有Grilamid PA12 TR90塑胶粒销售，为您提供详细的瑞士EMS化学PA12(尼龙12)TR90资料以及报价。
浏览量：5643 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：5590 -
TRITAN(美国伊士曼)TX1501HF/PCTG(共聚聚酯···美国伊士曼TRITAN PCTG TX1501HF 是一种伊士曼TRITAN的高流动级材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相对于伊士曼TRITAN共聚酯TX1001，其他突出的特点包括良好的韧性，水解稳定性，耐热性
浏览量：5489 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：5457 -
COC(环烯烃共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一种烯烃聚合物(COP)具有优异的光学性能，可用于制造相机和激光打印机的光学部件，比重是1.01g/cm(ASTM D792)，熔流率（熔体流动速率）(280C/2.16 kg)是25g/10 min，ZEO
浏览量：5447
推荐文章
-
XYRON(采龙)S202A|旭化成|PPO(聚苯醚)物性表参数
旭化成XYRON PPO S202A 是一种低粘度PPE原粉，特点: 良好的耐热性、尺寸稳定性和机械性能，应用领域: 汽车零件，电气和电子零件，工业零件，高性能等级实例: 具有很高的流动性，模
-
TPE/K TC7FLZ/TPE物性参数
德国胶宝Kraiburg THERMOLAST TPE K TC7FLZ 物性参数 K TC7FLZ是德国胶宝公司Kraiburg THERMOLAST塑性弹性体TPE型号之一 德国胶宝Kraiburg THERMOLAST TPE K TC7FLZ 物性参数 以下是德国胶宝Kraiburg THERMOLAST TPE
-
POK(脂肪族聚酮)M330S|晓星(POKETONE)物性表参数
晓星(POKETONE)POK M330S是一种抗UV注塑成型脂肪族聚酮树脂，是能够使用于汽车燃油输送管路、内外部装修材料、电子电器部件、气体阻隔包装材料、管子等多种用途的ENPLA材料。以下是POK(脂肪族聚酮)M330S|晓星(POKETONE)物性表参数物理性能额定值单位制测试方法比重 1.24g/cm³ASTM D792熔流率（熔体流动速率） (240°C/2.16
-
PC(聚碳酸酯)EM3022U/Samyang(三养)物性表参数
Samyang(三养)TRIREX PCEM3022U是一种非强化,冲击补强聚碳酸酯，比重是1.20g/cm³，熔流率（熔体流动速率）(300°C/1.2 kg)10g/10min，有着优异的机械特性，很好的尺寸稳定性及良好的电气特性，应用于工业材料,电子电器。以下是PC(聚碳酸酯)EM3022U/Samyang(三养)物性表参数PROPERTYUNITASTM METHODTYPICAL DATAPhysi
-
TPU(热塑性聚氨酯)58237/路博润(Lubrizol)物性表参数
路博润(Lubrizol)ESTANE TPU 58237是一种聚醚型热塑性聚氨酯，肖氏硬度90A，特点是透湿率高，良好的物理性能和弹性，专为性能优异的挤塑和注塑部件而设计，主要用于挤塑和注塑应用。以下是TPU(热塑性聚氨酯)58237/路博润(Lubrizol)物性表参数原厂资料ESTANE 58237.pdf成型方式薄膜挤出吹塑技术参数物理性能值/单位测试标准测
-
POE(聚烯烃弹性体)6902/埃克森美孚(ExxonMobil)物性表参数
埃克森美孚(ExxonMobil)Vistamaxx(威达美)POE 6902是一种高性能聚合物，主要由乙烯随机分布的等聚丙烯重复单元组成，采用埃克森美孚专有的茂金属催化剂技术生产，熔体流动速率(230°C/2.16kg)是100克/10分钟，密度(23°C)是0.869克/厘米³，它具有很好的弹性，易于加工，并且可与各类材料相容，尤其适用于需要优异的填料分
-
TPE(热塑性弹性体)TF7BTL/凯柏胶宝/物性表参数
凯柏胶宝KRAIBURG热塑宝K TPE TF7BTL 是一款半透明, 硬度69A的TPE材料,用于食品接触应用的自然色和半透明材料解决方案。该系列的特点包括卓越的PP包胶性能，典型应用：剃须刀、功能和设
-
PC(聚碳酸酯)RX1452|科思创(Covestro)物性表参数
科思创Makrolon PC RX1452是全球品级; 体积熔融指数10 厘米3/10分钟,低粘度;应用于医疗设备，easy release。德国科思创Makrolon PC RX1452物性表参数PDF文档浏览以下是PC(聚碳酸酯)RX1452/科思创/物性表参数物理性能额定值单位制测试方法密度 (23°C)1.20g/cm³ISO 1183表观密度 10.66g/cm³ISO 60熔流率（熔体流动速率） (
-
PA46(尼龙46)TW441|恩骅力(Envalior)物性表参数
恩骅力(Envalior)(原帝斯曼DSM)Stanyl聚合物PA46 TW441是一款加30% 玻纤增强, 可电镀,热稳定性或耐热性良好,含脱模剂,高粘度注塑成型的PA46原料，应用于、滑动导轨耐摩擦面导轨、正时链张紧器、正时链张紧器摩擦面，Stanyl作为高性能聚酰胺,在对耐热性、设计硬度、摩擦磨耗以及流动性都有要求的严苛的应用中表现优异，Stany
-
PP(聚丙烯)S2035/台化(TAIRIPRO)物性表参数
台化(TAIRIPRO)PP S2035是一种纤维级聚丙烯，比重是0.900g/cm³，熔流率（熔体流动速率）(230°C/2.16 kg)是34.0g/10min，特点是透明性佳、柔软性佳，应用于短纤、滤布 、複丝 。以下是PP(聚丙烯)S2035/台化(TAIRIPRO)物性表参数基本信息特性均聚物机构评级EC 1907/2006 (REACH)FDA 21 CFR 177.1520RoHS 合规性RoHS 合规形式