PA6(尼龙6)BTC65H3.0EF/德国朗盛/物性表参数

日期：2020-04-14 10:15:16 编辑：科思德塑胶来源：科思德塑胶浏览：327

德国朗盛LANXESS Durethan PA6 BTC65H3.0EF是一种加入65%矿物填充，注塑，提高导热，热老化稳定尼龙6树脂，尼龙从环境中吸收潮气的能力也不同,这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
PA6 BTC65H3.0EF

以下是PA6(尼龙6)BTC65H3.0EF/德国朗盛/物性表参数

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.70
	Molding shrinkage, transverse	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.75
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.15
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.15
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	9900	3500
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	90	50
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3	5
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	45	35
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	25	20
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	<10	<10
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	35	25
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	25	20
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	<10	<10
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	10000	3800
	Flexural strength	2 mm/min	MPa	ISO 178-A	160	75
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.6	4
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	155	70
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	221
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	145
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	190
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	208
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.5
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.6
	Thermal conductivity, with flow		W/(m·K)	ISO 22007-4	1.3
	Thermal conductivity, through-plane		W/(m·K)	ISO 22007-4	1.0
	Glow wire test (GWFI)	0.75 mm	°C	IEC 60695-2-12	900
	Glow wire test (GWFI)	1.5 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	3.0 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWIT)	0.75 mm	°C	IEC 60695-2-13	750
	Glow wire test (GWIT)	1.5 mm	°C	IEC 60695-2-13	750
	Glow wire test (GWIT)	3.0 mm	°C	IEC 60695-2-13	750
Electrical properties (23 °C/50 % r. h.)
	Volume resistivity		Ohm·m	IEC 60093	1.00E+15
	Surface resistivity		Ohm	IEC 60093	6.00E+13
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	600
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	3.4
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1
	Density		kg/m³	ISO 1183	2005
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	290
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	280-300
	Mold temperature		°C	-	80-120

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.

上一页：PA6(尼龙6)BM430H2.0/德国朗盛/物性表参数下一页：PA6(尼龙6)BTC75H3.0EF/德国朗盛/物性表参数

返回首页返回物性参数列表

PA6(尼龙6)BTC65H3.0EF/德国朗盛/物性表参数