VALOX(沙伯基础)4022/PBT热塑性聚酯/物性表参数
沙伯基础创新塑料SABIC的VALOX 4022 PBT是一种加20%高强度玻璃纤维增强PBT注塑树脂，具有良好的机械性能,用途:射灯，电器外壳和把手。
 |
沙伯基础创新塑料的VALOX 4022 PBT物性表参数PDF文档下载 |
以下是VALOX(沙伯基础)4022/PBT热塑性聚酯/物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 120 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 120 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 7400 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 170 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 170 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5900 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 120 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 120 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 7300 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 180 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 175 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 6200 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 130 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 122 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 42 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 42 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 560 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 560 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 75 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 75 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 75 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 8 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 200 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 3.07E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 7.32E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 3.04E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.78E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 210 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 220 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 205 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 200 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.45 | - | ASTM D 792 | |
| Filler Content | 20 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.7 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.4-1 | % | SABIC method | |
| Melt Flow Rate, 266°C/5.0 kgf | 40 | g/10 min | ASTM D 1238 | |
| Density | 1.45 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.15 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.03 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 16 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 23 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 30 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 140 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.6 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.015 | - | ASTM D 150 | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.6 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.015 | - | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.2 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Compliant, 94HB Flame Class Rating | 0.84 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：9193 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：9131 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：8405 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：7354 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：6769 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：6232 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：5856 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：5701 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：5605 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：5365 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：5194 -
COC(环烯烃共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一种烯烃聚合物(COP)具有优异的光学性能，可用于制造相机和激光打印机的光学部件，比重是1.01g/cm(ASTM D792)，熔流率（熔体流动速率）(280C/2.16 kg)是25g/10 min，ZEO
浏览量：5176 -
PA12(尼龙12)TR90|瑞士EMS化学|物性表参数科思德塑胶网站提供瑞士EMS化学PA12 TR90的物性表参数下载，并且有Grilamid PA12 TR90塑胶粒销售，为您提供详细的瑞士EMS化学PA12(尼龙12)TR90资料以及报价。
浏览量：5115 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：5067 -
TRITAN(美国伊士曼)TX1501HF/PCTG(共聚聚酯···美国伊士曼TRITAN PCTG TX1501HF 是一种伊士曼TRITAN的高流动级材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相对于伊士曼TRITAN共聚酯TX1001，其他突出的特点包括良好的韧性，水解稳定性，耐热性
浏览量：5034
推荐文章
-
PC(聚碳酸酯)3025U/Samyang(三养)物性表参数
Samyang(三养)TRIREX PC3025U是一种非强化,耐气候聚碳酸酯，比重是1.20g/cm³，熔流率（熔体流动速率）(300°C/1.2 kg)10g/10min，有着优异的机械特性，很好的尺寸稳定性及良好的电气特性，应用于汽车内饰,汽车外饰,杂货,电子电器。以下是PC(聚碳酸酯)3025U/Samyang(三养)物性表参数PROPERTYUNITASTM METHODTYPICAL D
-
PA66(尼龙66)A3ZG5|BASF(巴斯夫)物性表参数
巴斯夫ULTRAMID PA66 A3ZG5 是一种冲击改性，加玻璃纤维25%增强注射成型等级，具有良好的尺寸稳定性，巴斯夫尼龙是以聚酰胺为基础的聚酰胺成型化合物，由于它们良好的性质 ，这些
-
Apec（雅霸）1703|科思创|PC（聚碳酸酯）物性表参数
Apec（雅霸）1703科思创/PC（聚碳酸酯）物性表PDF文档下载Apec（雅霸）1703科思创/PC（聚碳酸酯）物性表参数物理性能额定值单位制测试方法密度 (23°C)1.17g/cm³ISO 1183熔流率（熔体流动速率） (330°C/2.16 kg)17g/10 minISO 1133溶化体积流率（MVR） (330°C/2.16 kg)17.0cm³/10minISO 1133收缩率 1ISO 294-4&nb
-
PP(聚丙烯)RP316M/利安德巴塞尔/物性表参数
利安德巴塞尔(Lyondellbasell)Moplen PP RP316M是一种微改性聚丙烯无规共聚物，熔体流动速率(230°C/2.16kg)是8克/10分钟，密度(23°C)是0.9克/厘米³，Moplen RP316M通常被客户用于制造无取向铸造薄膜，客户报告固定，层压，纺织和食品包装的典型应用，客户反映，moplen RP316M具有非常好的加工性，用mopen RP316M生产的
-
PC(聚碳酸酯)D451/沙伯基础(SABIC)物性表参数
沙伯基础(SABIC)LNP Thermocomp PC D451是一种加玻璃纤维增强聚碳酸酯树脂，密度是1.52g/cm³，熔体流动速率(300°C/1.2 kg)是18g/10min，该材料的附加特性包括该材料具有模数高、平整度好、延展性好、无溴、无氯阻燃等特点。以下是PC(聚碳酸酯)D451/沙伯基础(SABIC)物性表参数基本信息黄卡编号E207780-101265025填料/增强材
-
TPEE/XFR440/TPEE物性表参数
泰科纳Riteflex弹性体TPEE XFR440物性表参数 Celanese Riteflex TPEE XFR 440 The property table is provided by www.cn-plas.com , welcome to download, reprint please indicate the source! Physical Properties 物理性质 Metric 公制数
-
PA6(尼龙6)BKV115H3.0/德国朗盛/物性表参数
德国朗盛 LANXESS Durethan PA6 BKV115H3.0 是一种加15%玻璃纤维，注塑成型，改善冲击强度，热老化稳定尼龙6树脂，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材
-
PBT(聚对苯二甲酸丁二酯)3405|宝理塑料|物性表参数
日本宝理DURANEX PBT 3405 是一种加玻纤45%, 缓燃, 标准的聚酯聚合物,由于它具有高的熔点和结晶度，由于其吸水率和线性热膨胀系数很低，因此具有优良的尺寸稳定性。此外，它的电绝缘性
-
TPE(热塑性弹性体)TF1STL/凯柏胶宝/物性表参数
凯柏胶宝KRAIBURG热塑宝K TPE TF1STL 是一款半透明, 硬度75VLRH的FC/S系列TPE材料,用于食品接触应用的极软材料,拥有自然色、半透明及高透明度品种可供选择,这些材料具有干燥的触感，典型应
-
PEEK(聚醚醚酮)4000P/赢创德固赛/物性表参数
赢创德固赛VESTAKEEP PEEK 4000P一种无增强，高粘度聚醚醚酮粉末，该产品适用于化合物的制造，也可用作复合材料制造的散粉，这种半结晶聚合物具有优异的耐热性和耐化学性。VESTAKEEP®4000p具有低可燃性。PEEK(聚醚醚酮)4000P/赢创德固赛物性表参数PDF文档下载生产商：赢创德固赛（品名：VESTAKEEP）以下是PEEK(聚醚醚酮)40