VALOX(沙伯基础)4031/PBT热塑性聚酯/物性表参数
沙伯基础创新塑料SABIC的VALOX 4031 PBT是一种加30%高强度玻璃纤维增强PBT注塑树脂，具有优异的强度、刚度和耐热性,用途:电器手柄、射灯、电机。
 |
沙伯基础创新塑料的VALOX 4031 PBT物性表参数PDF文档下载 |
以下是VALOX(沙伯基础)4031/PBT热塑性聚酯/物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 140 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 140 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 10000 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7900 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 135 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 135 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 10000 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 210 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 200 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 8300 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 125 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 125 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 65 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 60 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 880 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 880 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 100 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 100 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 100 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 55 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 55 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 11 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 12 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 12 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 50 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 55 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 2.1E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 3.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 1.98E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.73E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 215 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 220 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 205 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.54 | - | ASTM D 792 | |
| Filler Content | 30 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.7 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-1 | % | SABIC method | |
| Melt Flow Rate, 266°C/5.0 kgf | 50 | g/10 min | ASTM D 1238 | |
| Density | 1.54 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.26 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 12 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 30 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 40 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 150 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D 149 | |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 1 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 15 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.1 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.0016 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 0.84 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 6 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：13871 -
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：11825 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：11363 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：9446 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：8326 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：8219 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：7706 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：7190 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：7070 -
PA12(尼龙12)TR90|瑞士EMS化学|物性表参数科思德塑胶网站提供瑞士EMS化学PA12 TR90的物性表参数下载，并且有Grilamid PA12 TR90塑胶粒销售，为您提供详细的瑞士EMS化学PA12(尼龙12)TR90资料以及报价。
浏览量：6783 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：6730 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：6581 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：6476 -
PC(聚碳酸酯)L-1250Y|嘉兴帝人|物性表参数嘉兴帝人Panlite PC L-1250Y 是一款熔融体积流量是8MVR，特性是 脱模性能良好, 中等粘性 ，通用级应用，在Japan实现工业化生产的聚碳酸酯树脂，长期以来，帝人一直致力于其性能的提高和
浏览量：6421 -
TRITAN(美国伊士曼)TX1501HF/PCTG(共聚聚酯···美国伊士曼TRITAN PCTG TX1501HF 是一种伊士曼TRITAN的高流动级材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相对于伊士曼TRITAN共聚酯TX1001，其他突出的特点包括良好的韧性，水解稳定性，耐热性
浏览量：6398
推荐文章
-
PC/ABS(PC合金)GN5001SF|LUPOY(LG化学)物性表参数
LG工程塑料LUPOY PC/ABS GN5001SF详细介绍 PC/ABS GN5001SF 广泛使用的塑料更硬、更轻，是用作工业材料高功能性塑料工程塑料中的一种。聚碳酸脂也是防弹玻璃的材料，具有耐冲击性、耐热性、
-
PP(聚丙烯)SH52|韩华道达尔(Hanwha)物性表参数
韩华道达尔(Hanwha)高光泽PP SH52, SH51是耐冲击性优异的产品，它对于对光泽性和耐冲击性有要求的电热产品保持了良好的平衡，和一般Homo PP相比，刚性, 耐冲击性高，长期热稳定性优异。可以应用于对这些特性有要求的电热器具零件,并可用于食品用途以及和食品有关的零件,其特点：高光泽复合PP SH51, SH52型号适用于电热器具时
-
POM(聚甲醛树脂)HC760|旭化成(AsahiKASEI)物性表参数
旭化成(AsahiKASEI)Tenac-C(铁耐克-C) POM HC760是防刮擦等级,高性能，标准中粘度的聚甲醛树脂，密度 1.41(g/cm³)，弯曲模量2750 (MPa) ，简支梁缺口冲击强度6.0(kJ/m²) ，典型用途领域包括工程/工业配件和房屋。Tenac-C(铁耐克-C) POM HC760物性表参数PDF文档下载生产商：日本旭化成、品名：Tenac-cPOM中文名称：(聚甲醛
-
POM(聚甲醛树脂)GA510|旭化成|物性表参数
旭化成(AsahiKASEI)TENAC(铁耐克)POM GA510是加10%玻纤增强具有高刚性和尺寸稳定性的聚甲醛树脂，密度 1.50(g/cm³)，弯曲模量3200(MPa) ，简支梁缺口冲击强度4.0(kJ/m²) ，典型用途领域包括工程/工业配件、房屋和汽车行业。TENAC GA510 POM物性表参数PDF文档下载以下是POM(聚甲醛树脂)GA510|旭化成|物性表参数物理性能额
-
PBT(聚对苯二甲酸丁二酯)315NFK|宝理塑料|物性表参数
日本宝理DURANEX PBT 315NFK 是一种加玻纤15%, 非卤素阻燃剂使用, 高电弧性,CTI/PLC:0的聚酯聚合物,由于它具有高的熔点和结晶度，由于其吸水率和线性热膨胀系数很低，因此具有优良的尺寸稳
-
PEEK(聚醚醚酮)4000CF30/赢创德固赛/物性表参数
赢创德固赛VESTAKEEP PEEK 4000CF30是加30%碳纤维增强材料聚醚醚酮、这种半结晶聚合物具有优异的耐热性和耐化学性，采用VESTAKEEP 4000CF30制造的部件具有阻燃性能，4000CF30可在普通热塑性塑料设备上加工，我们建议在注塑过程中熔体温度在370°C-380°C之间，模具温度应在160°C~200°C范围内，保持在180°C。PEEK(聚醚醚酮
-
PA66(尼龙66)MR001|Leona(尼胺龙)|旭化成|物性表参数
旭化成Leona(尼胺龙)PA66 MR001是一种40%的矿物填充的尼龙66材料，良好的耐热性，高刚性，低翘曲性，低变形，比重是1.52g/cm³，应用于插座。以下是PA66(尼龙66)MR001/Leona(尼胺龙)/旭化成/物性表参数填料/增强材料矿物填料添加剂热稳定剂特性尺寸稳定性良好刚性，高
-
PC(聚碳酸酯)HL6157/万华化学/物性表参数
万华化学Clarnate PC HL6157是一种聚碳酸酯无色透明，耐热，抗冲击，抗紫外线，流动溶指是16,广泛用于外壳（手提机器、家电、电子机器）、充电池外壳、托盘（低温仓库）、室外安装机器外壳等。以下是PC(聚碳酸酯)HL6157/万华化学/物性表参数产品特性易脱模抗紫外线中粘度颜色形状粒状透明成型方式注塑技术参数物理性能值/单
-
PC/ABS(PC+ABS合金) XCY630|沙伯基础|物性表参数
SABIC(沙伯基础)CYCOLOY PC/ABS XCY630 是水解稳定，标准黑色和自然色的PC/ABS混合料，提供良好的流动和优异的冲击。 PC/ABS XCY630物性表参数PDF文档下载 以下是SABIC 合金塑料PC/ABS Cycoloy XCY630 物性
-
PC(聚碳酸酯)FST3403/沙伯基础/物性表参数
LEXAN PC FST3403 树脂是一种高流量的PC共聚物树脂，适用于注塑成型。这种无卤阻燃树脂是EN45545 R6 HL3兼容的，是列车内部应用(R6)的理想候选。它还满足DIN5510-2、NFPA-130和PN-K-02511标准的要求