VALOX(沙伯基础)420/PBT热塑性聚酯/物性表参数
沙伯基础创新塑料SABIC的VALOX 420 PBT是一种加30%GR，具有优异的强度、刚度和尺寸稳定性,高耐热性,产品电器手柄，聚光灯，电动马达，连接器。
 |
沙伯基础创新塑料的VALOX 420 PBT物性表参数PDF文档下载 |
以下是VALOX(沙伯基础)420/PBT热塑性聚酯/物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 145 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 145 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 10300 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8000 | MPa | ASTM D 790 | |
| Taber Abrasion, CS-17, 1 kg | 19 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 135 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 135 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 10250 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 205 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 200 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 4 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 8500 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 125 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 120 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 55 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 50 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 970 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 970 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 110 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 105 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 105 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 45 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 10 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 9 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -40°C | 5 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 11 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 11 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 210 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D 648 | |
| Thermal Conductivity | 0.19 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 2.09E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.67E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.05E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.78E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 215 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 205 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.53 | - | ASTM D 792 | |
| Filler Content | 30 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.7 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-1 | % | SABIC method | |
| Melt Flow Rate, 266°C/5.0 kgf | 55 | g/10 min | ASTM D 1238 | |
| Density | 1.53 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.26 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 12 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 30 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 45 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 130 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | ASTM D 149 | |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 1 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, shorttime, 1.0mm | 19 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.1 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 | |
| Comparative Tracking Index | >600 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 0.84 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 6 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 775 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 3.0 mm | 825 | °C | IEC 60695-2-13 | |
| Injection Molding | ||||
| Drying Temperature | 120 | °C | ||
| Drying Time | 3-4 | hrs | ||
| Drying Time (Cumulative) | 12 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250-265 | °C | ||
| Nozzle Temperature | 245-260 | °C | ||
| Front - Zone 3 Temperature | 250-265 | °C | ||
| Middle - Zone 2 Temperature | 245-260 | °C | ||
| Rear - Zone 1 Temperature | 240-255 | °C | ||
| Mold Temperature | 65-90 | °C | ||
| Back Pressure | 0.3-0.7 | MPa | ||
| Screw Speed | 50-80 | rpm | ||
| Shot to Cylinder Size | 40-80 | % | ||
| Vent Depth | 0.025-0.038 | mm |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：10331 -
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：9524 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：8868 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：7655 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：7055 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：6617 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：6302 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：5877 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：5847 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：5546 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：5446 -
PA12(尼龙12)TR90|瑞士EMS化学|物性表参数科思德塑胶网站提供瑞士EMS化学PA12 TR90的物性表参数下载，并且有Grilamid PA12 TR90塑胶粒销售，为您提供详细的瑞士EMS化学PA12(尼龙12)TR90资料以及报价。
浏览量：5427 -
COC(环烯烃共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一种烯烃聚合物(COP)具有优异的光学性能，可用于制造相机和激光打印机的光学部件，比重是1.01g/cm(ASTM D792)，熔流率（熔体流动速率）(280C/2.16 kg)是25g/10 min，ZEO
浏览量：5361 -
TRITAN(美国伊士曼)TX1501HF/PCTG(共聚聚酯···美国伊士曼TRITAN PCTG TX1501HF 是一种伊士曼TRITAN的高流动级材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相对于伊士曼TRITAN共聚酯TX1001，其他突出的特点包括良好的韧性，水解稳定性，耐热性
浏览量：5326 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：5291
推荐文章
-
TRITAN(美国伊士曼)LX150HF/PCTG(共聚聚酯)物性表参数
美国伊士曼TRITAN PCTG LX150HF 是是一种无定形共聚酯的高流度，具有优异的外观和清晰度,LX150HF粘度降低40 - 50%的相对于标准等级的伊士曼TRITAN,其最突出的特点是优良的韧性、水解稳定性、
-
PA66(尼龙66)6210GC|惠州南亚塑胶|物性表参数
南亚塑胶工业（惠州）(Nan Ya Plastic)PA66 6210GC是一种高强度, 加入玻纤增强的尼龙66(PA66)树脂，耐磨损性良好，耐热性良好，耐疲劳性能，产品用途：断电器、电器箱外壳、插头插座、绕线轴。以下是PA66(尼龙66)6210GC|惠州南亚塑胶|物性表参数机械性能额定值单位测试方法拉伸强度2000kg/cmASTM D638弯曲弹性率85000kg/cmA
-
LCP(工业化液晶聚合物)E481i|日本宝理|物性表参数
日本宝理LAPEROS LCP E481i是一种低翘曲性, 低异向性的工业化液晶聚合物,密度1.77g/cm³，拉伸强度115MPa，颜色有：VF2201/BK210P ，阻燃性UL94-V-0,这种材料不但具有不同数量级的机械强度，而且还具有随着其壁厚的变薄，相对强度反而增加的特异的性能，并且其线性热膨胀率接近金属材料。LCP(工业化液晶聚合物)E481i/日本宝
-
PTFE(聚四氟乙烯)F-201/大金氟化工/物性表参数
大金氟化工(POLYFLON)PTFE F-201是一种成型粉末聚四氟乙烯树脂（polytetrafluoroethylene）(分散树脂)，平均粒径500(μm)，表观密度0.45(g/ml)，熔融粘度是10¹⁰~10¹¹poise(380℃)，连续使用温度是260℃，因其摩擦系数非常小，所以具有优异的自润滑性，由于表面张力很低，所以具有优异的防水防油性和不粘性，由于不含有
-
XYRON(采龙)G701H|旭化成|PPO(聚苯醚)物性表参数
旭化成XYRON PPO G701H 是一种加入10%玻璃纤维增强PPE/PS原料，特点: 良好的耐热性、尺寸稳定性和机械性能，应用领域: 汽车零件，电气和电子零件，工业零件，高性能等级实例: 具有很
-
PP(聚丙烯)BI451/韩华道达尔/物性表参数
韩华道达尔嵌段 PP BI451 是用于注塑用途的嵌段共聚PP，采用韩华道达尔HIPP技术生产.其特点是：优异的刚性/冲击平衡性、高流动性。 韩华道达尔PP BI451物性表参数PDF文档下载 以下是 韩
-
PC(聚碳酸酯)LDS3722|三菱工程塑料|物性表参数
三菱工程塑料XANTAR PC LDS3722是灰色镭雕级别的聚碳酸酯,体积熔融指数12厘米3/10分钟; 密度是1.29cm³/10min，拉伸模量是2500MPa，维卡软化温度122°C, 特性是：激光标记 ;磷含量，低（到无） ;无溴阻燃性，被广泛地用于各种工业生产，如运动器械、汽车部件、光学仪器、机械、办公自动化设备和电子设备，获得了客户的广泛信
-
TPE(热塑性弹性体)OC8OAZ/凯柏胶宝/物性表参数
凯柏胶宝KRAIBURG尼塑宝 TPE OC8OAZ 是一款耐化学TPE,硬度是79A黑色TPE材料,AD/PAX/CR系列是用于电子应用中的双组件密封和机器工具中软质把手和手柄的材料解决方案。该材料拥有卓越的耐护肤
-
PMMA(压克力)CM-205M/奇美实业/物性表参数
奇美实业ACRYREX PMMA CM-205M 是光学级PMMA压克力树脂,熔融指数是3g/10min,用途是照明產品二次光學之原料,奇美压克力(ACRYREX)，乃是奇美公司，以其三十年制造压克力板之经验，引进美国连续
-
PC（聚碳酸酯）EXL1494T|沙伯基础|物性表参数
沙伯基础LEXAN PC EXL1494T聚碳酸酯(PC)硅氧烷共聚物树脂是注射成型级与FDA和欧盟食品接触合规，该树脂具有很低温(-40℃)延展性，结合介质流动特性，改进的释放和优异的加工性能，与标准PC相比，IM周期时间更短，LEXAN EXL1494T树脂可提供透明和不透明的颜色，是广泛的食品接触应用的材料。以下是PC（聚碳酸酯）EXL1494T/沙